Epocast 35-A/9216
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Huntsman Advanced Materials |
| Trademark: | Epocast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mQGxHE_Epocast-35-A-9216.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DESCRIPTION: EpoCast® 35-A/9216 resin is a two component, amber colored laminating resin designed for foundry applications and core supports, bonding fixtures, die facing for shaping heated metals and high temperature tools for urethane foaming. EpoCast® 35-A/9216 resin features excellent wetability of glass fabrics, quick setting at room temperature and excellent ser\/iceability up to 400°F. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 0.990 | g/cm³ | ASTM D792 |
| -- | 1.14 | g/cm³ | ASTM D792 |
| -- 2 | 1.19 | g/cm³ | ASTM D792 |
| Shrinkage 3 | 0.10 | % | ASTM D696 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 91 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus 4(25°C) | 24.1 | MPa | ASTM D790 |
| Flexural Strength 5(25°C) | 552 | MPa | ASTM D790 |
| Compressive Strength (25°C) | 414 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 143 | °C | ASTM D648 |
| CLTE - Flow | 1.5E-5 | cm/cm/°C | ASTM D696 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 25 | ||
| Shelf Life (25°C) | 52 | wk | |
| Thermoset Mix Viscosity | ASTM D2196 | ||
| -- 6 | 4000 | cP | ASTM D2196 |
| -- 7 | 3200 | cP | ASTM D2196 |
| -- | 3800 | cP | ASTM D2196 |
| Additional Information |
|---|
| CURE SCHEDULE: Twenty-four hours at room temperature, plus two hours at maximum service temperature. May be accelerated with heat. |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 8(25°C) | 60 | min |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Resin |
| 3 . | Laminate after three hours at 150°F aging |
| 4 . | Glass Laminate, Vacuum Cure |
| 5 . | Glass Laminate, Vacuum Cure |
| 6 . | Hardener |
| 7 . | Resin |
| 8 . | 100 gms |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SI-LINK™ AC DFDA-5488 NT | The Dow Chemical Company | PE, Unspecified | SI-LINK™ |
| NOVACARB NC-8020 | NOVA Polymers, Inc. | PC+ABS | NOVACARB |
| Addisil™ 482 E | Momentive Performance Materials Inc. | Rubber | Addisil™ |
| Bayblend® FR3015 | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| CGPC PVC R-10X MI Extrusion | China General Plastics Corporation | PVC, Flexible | CGPC PVC |