Sarlink® TPE ML-2355B
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mPgo20_Sarlink-TPE-ML-2355B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sarlink ML-2355B is a UV resistant TPE suitable for automotive interior injection molding applications. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 5 sec, Injection Molded) | 55 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow (100% Strain) | 1.20 | MPa | ISO 37 |
| Tensile Strength - Across Flow (Break) | 7.80 | MPa | ISO 37 |
| Tensile Elongation - Across Flow (Break) | 850 | % | ISO 37 |
| Compression Set (70°C, 22 hr) | 40 | % | ISO 815 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary, 206 1/s (200°C) | 168 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 200 | °C | |
| Front Temperature | 200 - 220 | °C | |
| Nozzle Temperature | 210 - 230 | °C | |
| Processing (Melt) Temp | 200 - 230 | °C | |
| Mold Temperature | 10.0 - 60.0 | °C | |
| Injection Pressure | 6.00 - 12.0 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 4.00 - 6.00 | MPa | |
| Back Pressure | 0.500 - 2.00 | MPa | |
| Screw Speed | 50 - 120 | rpm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets 2 to 4 hours at 65 degrees Celsius.Time SettingsInjection Time: 0.5-2 secondsHolding Time: 1-10 secondsCooling Time: As short as possible. The parts should be removable without deformation or piercing of the ejector(s) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCW-45H-12 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Fainplast PVC PH 45/N | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Kumho PS HI 425EH | Korea Kumho Petrochemical Co., Ltd. | PS (HIPS) | Kumho PS |
| Idemitsu PS NS-050 | Idemitsu PS | PS (HIPS) | Idemitsu PS |
| Karina IVORY PVC COMPOUND 900-35/2-P-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |