XYLEX™ X8409AC resin
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | XYLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mP6sY1_XYLEXX8409ACresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC + Polyester, Injection (Blow) Molding, or Extrusion Blow molding grade, Chemical Resistance and Transparency |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 4.8 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/2.16 kg) | 3.80 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.50 - 0.80 | % | Internal method |
| Transverse flow : 3.20mm | 0.50 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.37 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.13 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2370 | MPa | ASTM D638 |
| -- | 2180 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 57.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 55.0 | MPa | ASTM D638 |
| Fracture | 60.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 5.8 | % | ISO 527-2/50 |
| Fracture 5 | 92 | % | ASTM D638 |
| Fracture | 120 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2220 | MPa | ASTM D790 |
| -- 7 | 2000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 89.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 94.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 200 | J/m | ASTM D256 |
| 23°C | 850 | J/m | ASTM D256 |
| -30°C 10 | 8.0 | kJ/m² | ISO 180/1A |
| -10°C 11 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 10 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 70.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 116 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 104 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 13 | 102 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 123 | °C | ASTM D1525, ISO 306/B120 10 14 |
| -- | 121 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flow : 23 to 60°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : 23 to 60°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.23 | W/m/K | ISO 8302 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.576 | ASTM D542 | |
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | 1.5 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 - 87.8 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 5.0E-3 - 0.020 | % | |
| Cylinder Zone 1 Temp. | 235 - 260 | °C | |
| Cylinder Zone 2 Temp. | 235 - 260 | °C | |
| Cylinder Zone 3 Temp. | 235 - 260 | °C | |
| Cylinder Zone 4 Temp. | 235 - 260 | °C | |
| Cylinder Zone 5 Temp. | 235 - 260 | °C | |
| Adapter Temperature | 235 - 260 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 24 hrsHead - Zone 6 - Top Temperature: 241 - 271 °CHead - Zone 7 - Bottom Temperature: 241 - 271 °CHead - Zone 7 - Middle Temperature: 241 - 271 °CMelt Temperature (Parison): 249 - 271 °CMold Temperature: 32 - 77 °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 120*10*4 mm |
| 14 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® Electro 242-3 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| Ultradur® B 4040 G11 HMG BK15029 | BASF Corporation | PBT | Ultradur® |
| 4LEX® 10F03300 | 4Plas | PC | 4LEX® |
| Ferro PP LPP25BK51BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| Formolene® 2306N | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |