Reny® G16S
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mOnh2O_Reny-G16S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Reny® G16S is a Polyarylamide (PARA) material filled with 20% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Reny® G16S are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.43 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 8.8 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 6.10 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.15 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.12 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.1 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 20200 | 19900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 230 | 205 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.6 | 1.6 | % | ISO 527-2 |
| Flexural Modulus | 18800 | 18200 | MPa | ISO 178 |
| Flexural Stress | 338 | 294 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.4 | 4.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 50 | 39 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 240 | 234 | °C | ISO 75-2/A |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 275 | °C | |
| Middle Temperature | 280 | °C | |
| Front Temperature | 285 | °C | |
| Nozzle Temperature | 285 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2201H0 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Amilan® CM3001G-45 | Toray Resin Company | Nylon 66 | Amilan® |
| Chemlon® 233 G | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Hostacom TSOP EM5 D63104 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Karina MBU BLUEL -E 06/923-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |