Makrolon® GF8001
| Category: | PC , Polycarbonate |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makrolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mNxi0i_Makrolon-GF8001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MVR (300 °C/1.2 kg) 16 cm³/10 min; 20 % glass fiber reinforced; low viscosity; easy release; injection molding - melt temperature 310 - 330 °C; available in opaque colors only; housing parts |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.34 | g/cm³ | ISO 1183 |
| Apparent Density 1 | 0.64 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 19 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 16.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow | 0.30 to 0.50 | % | ISO 2577 |
| Flow | 0.30 to 0.50 | % | ISO 2577 |
| Across Flow : 2.00 mm 2 | 0.45 | % | ISO 294-4 |
| Flow : 2.00 mm 3 | 0.25 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.28 | % | |
| Equilibrium, 23°C, 50% RH | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 105 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 4(23°C) | 5800 | MPa | ISO 178 |
| Flexural Stress 5 | ISO 178 | ||
| 3.5% Strain, 23°C | 160 | MPa | |
| 23°C | 160 | MPa | |
| Flexural Strain at Flexural Strength 6(23°C) | 3.5 | % | ISO 178 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Shortname | ISO 7391-PC,MR,(,,)-18-3,GF20 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C, Complete Break) | 8.0 | kJ/m² | ISO 7391 |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C, Complete Break | 45 | kJ/m² | |
| 23°C, Complete Break | 50 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy (23°C) | 2.70 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force (23°C) | 700 | N | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 141 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 137 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 144 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 2.6E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 6.3E-5 | cm/cm/°C | |
| Thermal Conductivity 8(23°C) | 0.23 | W/m/K | ISO 8302 |
| RTI Elec (1.50 mm) | 80.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 80.0 | °C | UL 746 |
| RTI Str (1.50 mm) | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 36 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.30 | ||
| 23°C, 1 MHz | 3.30 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 1.0E-3 | ||
| 23°C, 1 MHz | 9.0E-3 | ||
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | 175 | V | |
| Solution B | 125 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 1.00 mm, BK | V-2 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 850 | °C | |
| 3.00 mm | 850 | °C | |
| Oxygen Index 9 | 32 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Pellets |
| 2 . | 60x60x2 mm, 500 bar |
| 3 . | 60x60x2 mm, 500 bar |
| 4 . | 2.0 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 2 mm/min |
| 7 . | Based on ISO 179-1eA, 3 mm |
| 8 . | Cross-flow |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PC 1005 GF 10 FL | TER HELL PLASTIC GMBH | PC | TEREZ PC |
| XYRON™ 740V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| UMG ALLOY® TC-25M | UMG ABS, Ltd. | PC+ABS | UMG ALLOY® |
| Formolene® L63568U | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| Thermec N™ 4314R40H | Technical Polymers, LLC | PPA | Thermec N™ |