LEXAN™ FL910 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mNtOM2_LEXAN-FL910-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Various weight reductions at 0.250" (6.35 mm) wall, 10% GR. High flexural strength and modulus, impact/heat resistant. V-0/5V at 0.250" (6.35 mm). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 1.12 | g/cm³ | ASTM D792 |
| -- | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (6.40 mm) | 0.40 - 0.60 | % | Internal method |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.16 | % | ASTM D570 |
| Equilibrium, 23°C | 0.32 | % | ASTM D570 |
| Foam - Physical 2 | 10 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Mechanical 3 | 10 | % | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Impact 4 | 10 | % | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Thermal 5 | 10 | % | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Electrical 6 | 20 | % | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Flame Class Minimum Density | 850 | kg/m³ | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (6.40 mm) | 3170 | MPa | ASTM D638 |
| Tensile Strength (Yield, 6.35 mm) | 52.4 | MPa | ASTM D638 |
| Tensile Elongation (Break, 6.35 mm) | 4.8 | % | ASTM D638 |
| Flexural Modulus (6.40 mm) | 3520 | MPa | ASTM D790 |
| Flexural Strength (Yield, 6.40 mm) | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | 850 | J/m | ASTM D4812 |
| Dart Drop Impact (23°C) | 46.1 | J | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 141 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 133 | °C | ASTM D648 |
| CLTE - Flow (-40 to 95°C) | 3.2E-5 | cm/cm/°C | ASTM E831 |
| Specific Heat | 1200 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.13 | W/m/K | ASTM C177 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.1E+17 | ohms | ASTM D257 |
| Volume Resistivity | 2.4E+17 | ohms·cm | ASTM D257 |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 2.45 | ASTM D150 | |
| 1 MHz | 2.40 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 1.3E-3 | ASTM D150 | |
| 1 MHz | 6.5E-3 | ASTM D150 | |
| Arc Resistance 7 | PLC 7 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 5VA | UL 94 |
| Additional Information |
|---|
| Structural Foam Molding - Blowing Agent, Chemical System: FLC95Structural Foam Molding - Blowing Agent, Physical System: NitrogenStructural Foam Molding - Concentration Range (Blowing Agent): 3 - 5 %Structural Foam Molding - Drying Temperature (Blowing Agent): 104 °CStructural Foam Molding - Drying Temperature (Resin): 121 °CStructural Foam Molding - Drying Time (Blowing Agent): 4 hrsStructural Foam Molding - Drying Time (Resin): 3 - 4 hrsStructural Foam Molding - Drying Time (Resin, Cumulative): 48 hrsStructural Foam Molding - Front Temperature: 293 - 310 °CStructural Foam Molding - Melt Temperature: 288 - 316 °CStructural Foam Molding - Middle Temperature: 293 - 310 °CStructural Foam Molding - Mold Temperature: 71 - 93 °CStructural Foam Molding - Nozzle Temperature: 271 - 293 °CStructural Foam Molding - Rear Temperature: 254 - 266 °CStructural Foam Molding - Recommended Concentration (Blowing Agent): 1.5 % |
| Note Message | |
|---|---|
| 1 . | Foam molded |
| 2 . | 6.4 mm wt reduction |
| 3 . | 6.4 mm wt reduction |
| 4 . | 6.4 mm wt reduction |
| 5 . | 6.4 mm wt reduction |
| 6 . | 6.4 mm wt reduction |
| 7 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4605 | RTP Company | SPS | RTP |
| Shuman PC 920 | Shuman Plastics, Inc. | PC | Shuman PC |
| TAROLOX 10 K4 | Taro Plast S.p.A. | PBT | TAROLOX |
| COSMOPLENE® AX764 | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Copolymer | COSMOPLENE® |
| MACOMASS PVC MM-PVC I 1570 | MACOMASS Verkaufs AG | PVC, Flexible | MACOMASS PVC |