Kingfa PP-R009
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mNcmGt_Kingfa-PP-R009.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa PP-R009 is a Polypropylene material. It is available in Asia Pacific or North America. Important attributes of Kingfa PP-R009 are:
Typical application of Kingfa PP-R009: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.990 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 1.4 to 1.6 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, Injection Molded) | 28.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, Injection Molded) | 100 | % | ASTM D638 |
| Flexural Modulus 3(23°C, Injection Molded) | 1100 | MPa | ASTM D790 |
| Flexural Strength 4(23°C, Injection Molded) | 29.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 58 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm, Injection Molded) | 115 | °C | ASTM D648 |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | ||
| 1.60 mm | V-0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime 5490 | Prime PVC® | PVC, Rigid | Prime |
| Sylvin 8651-90 Clear 8289 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TOTAL Polyethylene HD 6081 | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| COPYLENE® CH120 | Phillips 66 | PP Homopolymer | COPYLENE® |
| LNP™ VERTON™ UX03320 compound | SABIC Innovative Plastics | PPA | LNP™ VERTON™ |