RTP ESD C 702
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mLw536_RTP-ESD-C-702.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3450 | MPa | ASTM D638 |
| Tensile Strength | 34.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 7.5 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength | 48.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 270 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 116 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 98.9 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, Values per RTP Company testing.) | HB | UL 94 |
| Additional Information |
|---|
| Tensile Elongation, ASTM D638: 5-10%Molding Shrinkage, Linear-Flow, ASTM D955, 3.175mm: 4-6mm/mStatic Decay, FTMS-4046.1, Mil B-81705C: <2.0 secondsVolume Resistivity, ASTM D257: <10E3 ohm-cmSurface Resistivity, ASTM D257: <10E6 ohm/sq |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 177 - 288 | °C | |
| Middle Temperature | 177 - 288 | °C | |
| Front Temperature | 177 - 288 | °C | |
| Mold Temperature | 23.9 - 51.7 | °C | |
| Injection Pressure | 68.9 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (PC) XP 41 R 20 GF | A. Schulman Europe | PC | POLYMAN® |
| Shin-Etsu Elastomer KEG-2000-20A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| HAIPLEN EP30 G6 BA | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| ICORENE® N9205 | ICO Polymers EMEA, A Division of A. Schulman | PET | ICORENE® |
| Karina WHITE PVC COMPOUND 105850-10/174-B-ISE-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |