LNP™ LUBRICOMP™ UX05051 compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mLEqkE_LNP-LUBRICOMP-UX05051-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Internally lubricated Polyphthalamide compound, containing Glass Fiber and PTFE. Added features include Heat Stabilized, Flame Retardant and Hot Water Moldable Also known as: LNP* LUBRICOMP* Compound UFL-4026 A FR HS HW Product reorder name: UX05051 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.76 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 138 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 10700 | MPa | ISO 178 |
| Flexural Stress | 188 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 273 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.0E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 5.2E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.400 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 321 | °C | |
| Middle Temperature | 304 to 321 | °C | |
| Front Temperature | 304 to 321 | °C | |
| Processing (Melt) Temp | 304 to 316 | °C | |
| Mold Temperature | 93.3 to 121 | °C | |
| Back Pressure | 0.344 to 0.690 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PS 430M | Nizhnekamskneftekhim Inc. | PS (GPPS) | NEFTEKHIM PS |
| Evolue™ SP2510 | Prime Polymer Co., Ltd. | LLDPE | Evolue™ |
| HONES® PPS HS-B7-2 | Guangdong Shunde Hones Polymer Material Co., Ltd. | PPS | HONES® |
| Petrothene® NA209009 | LyondellBasell Industries | LDPE | Petrothene® |
| Sylvin 9067-80 Grey 9474 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |