CALIBRE™ 2061-12
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mK8lwR_CALIBRE-2061-12.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 2061-12 resin is suitable for steam and ethylene oxide sterilization required by the health care industry. CALIBRE 2061-12 provides exceptional clarity, heat resistance, impact strength, processability, and has low contamination levels. CALIBRE 2061-12 resin is compliant with ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. This product contains mold release. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955, ISO 294-4 |
| Water Absorption | ASTM D570, ISO 62 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 73 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2220 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 62.9 | MPa | ASTM D638 |
| Yield | 62.9 | MPa | ISO 527-2/50 |
| Break | 73.7 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 3 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 4 | 150 | % | ASTM D638 |
| Break | 150 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2220 | MPa | ASTM D790 |
| -- | 2250 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 6 | 99.2 | MPa | ASTM D790 |
| -- | 92.5 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 46 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| 23°C | 750 | J/m | ASTM D256 |
| 23°C | 65 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256, ISO 180 | |
| Instrumented Dart Impact 7(23°C, Total Energy) | 82.2 | J | ASTM D3763 |
| Tensile Impact Strength | 378 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed | 140 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 126 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 130 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 129 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 136 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 147 | °C | ISO 306/B50 |
| CLTE - Flow | |||
| -40 to 82°C | 6.8E-5 | cm/cm/°C | ASTM D696 |
| -40 to 82°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| -- | 2.0E+17 | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength | 17 | kV/mm | ASTM D149, IEC 60243-1 |
| Dielectric Constant | |||
| 60 Hz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150, IEC 60250 | |
| 100 Hz | 3.00 | IEC 60250 | |
| Dissipation Factor | |||
| 50 Hz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 2.0E-3 | ASTM D150, IEC 60250 | |
| 100 Hz | 1.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 8(1.50 mm) | HB | UL 94 | |
| Oxygen Index 9 | 26 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542, ISO 489 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | Method I (3 point load), 2.0 mm/min |
| 6 . | Method I (3 point load), 2.0 mm/min |
| 7 . | 3.39 m/sec |
| 8 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 9 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SE-337M80 | SHIN-A T&C | Epoxy | SHIN-A |
| Aurora PVC AP1227 Series | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |
| Gallonprene® GP520-4504 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| INTENE® 60 AF | Versalis S.p.A. | PBR, Low Cis | INTENE® |
| Iupital® FB2025 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |