Makropol® PC A3 MF UV PRTA010 PC320 MSP
| Category: | PC , Polycarbonate |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Makropol® PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mIOVqv_Makropol-PC-A3-MF-UV-PRTA010-PC320-MSP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate in black color,medium-viscosity, FDA grade , ideal for injection molding, good set of thermal properties, electrical and mechanical. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.80 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.12 | % | |
| Equilibrium | 0.30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2400 | MPa | ASTM D638 |
| Tensile Strength (Break) | 70.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 120 | % | ASTM D638 |
| Flexural Modulus | 2400 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 910 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 131 | °C | ASTM D648 |
| Vicat Softening Temperature | 144 | °C | ASTM D1525 2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dissipation Factor (60 Hz) | 9.0E-4 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-2 | UL 94 | |
| Oxygen Index | 28 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 265 to 290 | °C | |
| Mold Temperature | 70.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TOSE 420 | Mitsubishi Chemical Performance Polymers, Inc. | SEBS | tefabloc® |
| ARCEL® ULV (1.5 pcf) | NOVA Chemicals | PS+PE | ARCEL® |
| KumhoSunny ABS HGX4500 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| LOXIM 830 12 HB | LOXIM Industries Private Limited | PP, Unspecified | LOXIM |
| TechnoMid PA6 S GF 30 GL | TechnoCompound GmbH | Nylon 6 | TechnoMid |