NAXELL™ PC110-10G
| Category: | PC , Polycarbonate |
| Manufacturer: | MRC Polymers, Inc. |
| Trademark: | NAXELL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mHgK4u_NAXELL-PC110-10G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
PC110-10G is available in natural and custom colors. Further information and details are available upon request.
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 - 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, 3.18 mm) | 76.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C, 3.18 mm) | 8.0 | % | ASTM D638 |
| Flexural Modulus (23°C, 3.18 mm) | 3450 | MPa | ASTM D790 |
| Flexural Strength (23°C, 3.18 mm) | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Instrumented Dart Impact 1(23°C, 3.18 mm, Total Energy) | 24.4 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 143 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 138 | °C | ASTM D648 |
| CLTE - Flow (-40 to 35°C) | 3.2E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 127 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Dew Point | < -17.8 | °C | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 327 | °C | |
| Middle Temperature | 299 - 327 | °C | |
| Front Temperature | 304 - 332 | °C | |
| Nozzle Temperature | 293 - 332 | °C | |
| Processing (Melt) Temp | 304 - 332 | °C | |
| Mold Temperature | 65.6 - 116 | °C | |
| Injection Pressure | 68.9 - 138 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.00 - 0.517 | MPa | |
| Screw Speed | 30 - 75 | rpm | |
| Cushion | 6.35 | mm |
| Injection instructions |
|---|
| Packing: 50 to 75% of injection pressureHold: 40 to 60% of injection pressureAir Flow Rate: 0.8-1.0 CFM per lb/hour resin processed |
| Note Message | |
|---|---|
| 1 . | 3.35 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ceramer 20 | Ceramer GmbH | PPSU | Ceramer |
| DOWLEX™ 2098P | The Dow Chemical Company | LLDPE | DOWLEX™ |
| HiFill® PP GF20 CC HS | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| POLYfill PP CIP15015 UV | Polykemi AB | PP, Unspecified | POLYfill |
| Sylvin 5170-85 Red 6222 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |