Akulon® K223-KMV6
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mHPSWe_Akulon-K223-KMV6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akulon® K223-KMV6 is a Polyamide 6 (Nylon 6) material filled with 30% mineral. It is available in Asia Pacific or Europe. Important attributes of Akulon® K223-KMV6 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.53 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.63 | -- | % | |
| Flow | 0.63 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.2 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.7 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 6600 | 3500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 70.0 | 40.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | 4.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 2.0 | 2.0 | kJ/m² | |
| 23°C | 2.0 | 2.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 35 | 35 | kJ/m² | |
| 23°C | 35 | 60 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 205 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 120 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 5.0E-5 | -- | cm/cm/°C | |
| Transverse | 5.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 25 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.60 | 10.0 | ||
| 1 MHz | 3.20 | 3.70 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 8.5E-3 | 0.30 | ||
| 1 MHz | 0.014 | 0.090 | ||
| Comparative Tracking Index | 375 | 375 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 3.00 mm | V-0 | -- | ||
| 1.50 mm | V-2 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.750 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.750 mm | 725 | -- | °C | |
| 3.00 mm | 775 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 225 to 235 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 235 to 250 | °C | |
| Nozzle Temperature | 235 to 255 | °C | |
| Processing (Melt) Temp | 245 to 265 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 5014L HPT-1 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| Reny® 1313H | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Vatpol 402 | Vatan Plastik San. Tic. AS | PP, Unspecified | Vatpol |
| Cardia Biohybrid™ H-M03 | Cardia Bioplastics™ | TPS+PP | Cardia Biohybrid™ |
| AVP™ RLL05CP | SABIC Innovative Plastics | PC | AVP™ |