Braskem PE HDB1052U1
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem IDESA |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mHHalo_BraskemPEHDB1052U1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HDB1052U1 is a high molecular weight copolymer grade developed for blow molding applications where a combination of good rigidity and high environmental stress cracking resistance (ESCR) is required. Applications: High performance blow molded containers typically of 1-60 liters capacity for packaging aggressive products. Process: Blow Molding |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 10 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||
| 50°C, 10% Adinol | 130 | hr | ASTM D1693 |
| 50°C, 100% Adinol | > 1000 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 26.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 300 | % | ISO 527-2 |
| Flexural Modulus | 1100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23 | kJ/m² | ISO 179 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Bottle Stress Crack Resistance (60°C) | 2.1 | day |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-765A | CHI MEI CORPORATION | ABS | POLYLAC® |
| ColorRx® TPE-T66A0RXTP | LTL Color Compounders, Inc. | TPE | ColorRx® |
| Hax™ HF 225F | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| LARIPUR® LPR 8025 | COIM S.p.A. | TPU-Polyester | LARIPUR® |
| LUVOCOM® 3-8985/BL/L | Lehmann & Voss & Co. | Nylon 6 | LUVOCOM® |