Versaflex™ CE 3120-80N Datasheet,TPE,PolyOne Corporation-SHANGHAI SUSHENG

Message
Versaflex™ CE 3120-80N is targeted for consumer electronics applications where excellent abrasion resistance, chemical resistance and silky feel are required. Versaflex™ CE 3120-80N can also overmold to a variety of substrates including PC, ABS, PC/ABS, and Copolyester.

General Information
Features	Special specifications
Uses	overmolding Soft touch application Consumer goods application field
RoHS Compliance	RoHS compliance
Appearance	Natural color
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.08	g/cm³	ASTM D792

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A, 10 sec)	79		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress (300% Strain, 23°C)	6.89	MPa	ASTM D412
Tensile Strength (Break, 23°C)	13.5	MPa	ASTM D412
Tensile Elongation (Break, 23°C)	750	%	ASTM D412

Fill Analysis	Nominal Value	Unit	Test Method
Apparent Viscosity (200°C, 11200 sec^-1)	32.0	Pa·s	ASTM D3835

Injection	Nominal Value	Unit
Drying Temperature	49 - 60	°C
Drying Time	3.0 - 4.0	hr
Suggested Max Moisture	0.020 - 0.030	%
Rear Temperature	177 - 188	°C
Middle Temperature	182 - 199	°C
Front Temperature	188 - 216	°C
Nozzle Temperature	193 - 221	°C
Processing (Melt) Temp	193 - 218	°C
Mold Temperature	13 - 54	°C
Back Pressure	0.00 - 0.345	MPa
Screw Speed	50 - 80	rpm

Injection instructions
Typical colorant letdown ratios are 50:1 to 25:1 - loading levels should be as low as possible to minimize the effect on adhesion. A high color match consistency can be obtained by the use of precolored compounds available from GLS. Concentrates based on PVC should not be used. The final determination of color concentrate suitability should be determined by customer trials. Contact GLS for more information on appropriate color concentrate base resins.Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).Versaflex CE 3120-80N should not be left in the barrel for extended idle periods (greater than 5 minutes).Suggested Dewpoint: -40°FHot Runners: 380°F-440°FHot Tip: 380°F-450°FInjection Speed: 0.5 to 2 in/sec1st Stage - Boost Pressure: 500 to 1,000 psi2nd Stage - Hold Pressure: 20-60% of BoostHold Time (Thick Part): 2 to 4 secHold Time (Thin Part): 1 to 2 sec

Injection instructions

Typical colorant letdown ratios are 50:1 to 25:1 - loading levels should be as low as possible to minimize the effect on adhesion. A high color match consistency can be obtained by the use of precolored compounds available from GLS. Concentrates based on PVC should not be used. The final determination of color concentrate suitability should be determined by customer trials. Contact GLS for more information on appropriate color concentrate base resins.Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).Versaflex CE 3120-80N should not be left in the barrel for extended idle periods (greater than 5 minutes).Suggested Dewpoint: -40°FHot Runners: 380°F-440°FHot Tip: 380°F-450°FInjection Speed: 0.5 to 2 in/sec1st Stage - Boost Pressure: 500 to 1,000 psi2nd Stage - Hold Pressure: 20-60% of BoostHold Time (Thick Part): 2 to 4 secHold Time (Thin Part): 1 to 2 sec

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	PolyOne Corporation
Trademark:	Versaflex™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	mHFZnX_VersaflexCE312080N.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
PROTEQ™ C16UST2Z	Marplex Australia Pty. Ltd.	PP Copolymer	PROTEQ™
RTP 387 TFE 10	RTP Company	PC	RTP
Ad-Tech Epoxy EL-318	Ad-Tech Plastic Systems Corp.	Epoxy	Ad-Tech Epoxy
LEXAN™ VR2920 resin	SABIC Innovative Plastics	PC	LEXAN™
Lumiplas® LD7000FT	LG Chem Ltd.	PC	Lumiplas®