TOTAL Polyethylene Lumicene® M 4707 EP
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mH0rE0_TOTAL-Polyethylene-Lumicene-M-4707-EP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lumicene® mPE M 4707 EP is a second generation metallocene based High Density Polyethylene with hexene as comonomer. Lumicene® mPE M 4707 EP can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The combination of these features brings a significant downgauging potential. Lumicene® mPE M 4707 EP is especially dedicated to film applications where high gloss and high transparency are required, particularly in blend and in coextrusion with LLDPE or LDPE. Lumicene® mPE M 4707 EP is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as bags, heavy-duty sacks, automatic packaging, mailing film and lamination. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.947 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, Blown Film | 24.0 | MPa | |
| TD : Yield, 40 µm, Blown Film | 25.0 | MPa | |
| MD : Break, 40 µm, Blown Film | 39.0 | MPa | |
| TD : Break, 40 µm, Blown Film | 38.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 40 µm, Blown Film | 610 | % | |
| TD : Break, 40 µm, Blown Film | 750 | % | |
| Dart Drop Impact (40 µm, Blown Film) | 80 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 40.0 µm | 10.0 | kN/m | |
| TD : 40.0 µm | 60.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 130 | °C | ISO 306 |
| Melting Temperature | 131 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 14 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VeroYellow RGD836 | Stratasys | Unspecified | VeroYellow |
| Nanjing Hongrui PA6 B201 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 6 | Nanjing Hongrui PA6 |
| Elastollan® 695A-15N | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyester | Elastollan® |
| INNOPOL® PP CS 2-4630 FR | Inno-Comp Ltd. | PP Impact Copolymer | INNOPOL® PP |
| Durethan® AKV 50 H2.0 901510 | LANXESS GmbH | Nylon 66 | Durethan® |