Kingfa APO-2004
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mGz1Gw_Kingfa-APO-2004.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa APO-2004 is a polypropylene material,. This product is available in the Asia-Pacific region,. The typical application field of Kingfa APO-2004 is: automobile industry |
| General Information | |
|---|---|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 - 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 - 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 1.0 - 1.3 | % | Internal method |
| Ash Content 1(800°C) | 20 | % | ISO 3451-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 29.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 4.00mm span | 118 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 4.00mm span | 66.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (3.00 mm) | 65 | mm/min | ISO 3795 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 180 - 210 | °C | |
| Middle Temperature | 190 - 230 | °C | |
| Front Temperature | 200 - 240 | °C | |
| Processing (Melt) Temp | 190 - 245 | °C | |
| Mold Temperature | 20.0 - 50.0 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 10.0 | MPa |
| Injection instructions |
|---|
| Processing Temp. Limit: 260°C |
| Note Message | |
|---|---|
| 1 . | 30 min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3403-1 | RTP Company | LCP | RTP |
| RAMOFIN PPH343T4BK11 | Polyram Ram-On Industries | PP Homopolymer | RAMOFIN |
| Sylvin 8815-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ALCUDIA® HDPE 51100 | REPSOL | HDPE | ALCUDIA® HDPE |
| LNP™ STAT-KON™ AE003 compound | SABIC Innovative Plastics Europe | ABS | LNP™ STAT-KON™ |