TORZEN® U4803 NC01
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | INVISTA Engineering Polymers |
| Trademark: | TORZEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mGcCFp_TORZEN-U4803-NC01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TORZEN® U4803 NC01 is a general purpose, natural PA66 resin suitable for compounding, injection molding, and extrusion applications where ease of processing, good color and physical property retention are desired. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.7 | % | |
| Flow : 2.00 mm | 1.3 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 84.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.5 | % | |
| Break | 50 | % | |
| Flexural Modulus | 3000 | MPa | ISO 178 |
| Flexural Stress | 98.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 3.7 | kJ/m² | |
| 23°C | 3.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength (23°C) | 5.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 205 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 73.0 | °C | ISO 75-2/A |
| Melting Temperature | 263 | °C | ISO 11357-3 |
| CLTE | DIN 53752 | ||
| Flow : 23 to 55°C, 2.00 mm | 4.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C, 2.00 mm | 1.0E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 8.0E+14 | ohms | IEC 60093 |
| Volume Resistivity (2.00 mm) | 3.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 33 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (4.00 mm) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.710 mm | 850 | °C | |
| 1.50 mm | 850 | °C | |
| 3.00 mm | 900 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.710 mm | 700 | °C | |
| 1.50 mm | 700 | °C | |
| 3.00 mm | 700 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 16 to 20 | hr | |
| Suggested Max Moisture | 0.080 to 0.18 | % | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Back Pressure | 0.200 to 1.00 | MPa | |
| Screw Speed | 75 to 180 | rpm | |
| Cushion | 4.00 to 6.00 | mm | |
| Vent Depth | 7.0E-3 to 0.040 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 FR NH | RTP Company | Nylon 66 | RTP |
| NORYL™ WCD801AU resin | SABIC Innovative Plastics Asia Pacific | PPE+TPE | NORYL™ |
| EPLAMID 6 CBR 30 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 6 | EPLAMID 6 |
| Hifax TRC 790P | LyondellBasell Industries | TPO (POE) | Hifax |
| MACOMASS PVC MM-PVC E 1570 | MACOMASS Verkaufs AG | PVC, Flexible | MACOMASS PVC |