Quadrant EPP Fluorosint® 207
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mGTayt_Quadrant-EPP-Fluorosint-207.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Quadrant EPP Fluorosint® 207 is a Polytetrafluoroethylene (PTFE) product filled with mica. It can be processed by compression molding and is available in Europe or North America. Applications of Quadrant EPP Fluorosint® 207 include engineering/industrial parts, sealing applications and food contact applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.30 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.00 mm | 0.030 | % | |
| Saturation, 23°C | 2.0 | % | |
| Water Absorption 1(23°C, 3.00 mm) | 4.0 | mg | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 10.0 mm) | 50 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1800 | MPa | ISO 527-2/1B/1 |
| Tensile Stress (Break) | 10.0 | MPa | ISO 527-2/1B/5 |
| Tensile Strain (Break) | 50 | % | ISO 527-2/1B/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 100 | °C | ISO 75-2/A |
| Continuous Use Temperature | |||
| -- 2 | 260 | °C | |
| -- 3 | 280 | °C | |
| Melting Temperature (DSC) | 327 | °C | |
| CLTE - Flow | |||
| -- | 1.0E-4 | cm/cm/°C | ASTM D696 |
| 23 to 100°C | 1.0E-4 | cm/cm/°C | |
| 23 to 150°C | 1.0E-4 | cm/cm/°C | |
| > 150°C | 1.4E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 8.0 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 2.65 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 8.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Oxygen Index | > 95 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Weight, 24 hrs |
| 2 . | 20000 hrs |
| 3 . | Short periods |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SWANCOR Epoxy CP99 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| Generic PPS - Mineral | Generic | PPS | Generic |
| LNP™ LUBRILOY™ RF203XXH compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |
| LNP™ STAT-LOY™ KX09024 compound | SABIC Innovative Plastics Europe | Acetal (POM) Copolymer | LNP™ STAT-LOY™ |
| LGG 1044 | LG Polymers India Pvt. Ltd. | PS (GPPS) | LGG |