TAROLOX 10 G3 X0
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mGHa7G_TAROLOX-10-G3-X0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PBT glass fiber reinforced 15%, self extinguishing UL94 V0 also at low thickness, good flow, good surface finish, good mechanical properties. UL94 V0 approuved all colors at 0,97 mm. UL746B approved Available: all colors, heat stabilized (H), release agent (W), without PBDE/PBDF. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 to 1.54 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 to 0.80 | % | |
| Across Flow | 0.80 to 1.0 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.050 | % | ASTM D570, ISO 62 |
| Saturation | 0.30 | % | ASTM D570 |
| Saturation, 23°C | 0.30 | % | ISO 62 |
| Granule Humidity | < 0.050 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5500 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 95.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 5500 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 140 | MPa | ISO 178 |
| Break | 140 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 60 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 210 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 190 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | |||
| -- | 75.0 | °C | UL 746B |
| -- 1 | 90.0 | °C | IEC 60216 |
| -- 2 | 120 | °C | IEC 60216 |
| -- 3 | 130 | °C | IEC 60216 |
| -- 4 | 160 | °C | IEC 60216 |
| Vicat Softening Temperature | |||
| -- | 210 | °C | ASTM D1525, ISO 306/A50 7 5 |
| -- | 205 | °C | ASTM D1525, ISO 306/B50 8 6 |
| Ball Pressure Test (215°C) | Pass | VDE 0470 | |
| Melting Temperature | 220 to 225 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 22 | kV/mm | ASTM D149 |
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | > 250 | V | |
| Solution B | 175 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.970 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 775 | °C | IEC 60695-2-13 |
| Oxygen Index | 28 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Pre-heater | 120 to 130 | °C | |
| Drying Time | |||
| -- | 1.0 to 2.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 20000 hrs |
| 2 . | Heat Stabilized, 20000 hrs |
| 3 . | Short Term |
| 4 . | Heat Stabilized, Short Term |
| 5 . | Rate A (50°C/h), Loading 1 (10 N) |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRISTAR® PC-10R-CL(V22) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| NILENE® E20 K25MX | Taro Plast S.p.A. | PP Copolymer | NILENE® |
| NYLOY® UB-0010N-V G55L2B | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| Dryflex® A3 700600 | ELASTO | SEBS+SBS | Dryflex® |
| Iupiace® AP4 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |