VITAMIDE® BX30WT6338 is a Polyamide 6 (Nylon 6) product. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | 1.5 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.90 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 60.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 10 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2750 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 100 | MPa | ISO 178 |
| Break | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 15 | kJ/m² | ISO 179 |
| Charpy Notched Impact Strength 1 | 14.5 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 2 | 50.0 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength | 50 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 200 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 220 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 3.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 6.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 | |
| Oxygen Index | 30 | % | ASTM D2863, ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SPESIN® KP212G30VFBL | Kolon Plastics, Inc. | PBT | SPESIN® |
| Fenochem C 4500 | Chemiplastica, Inc. | Phenolic | Fenochem |
| FRIANYL® A3 GF35 V0P1 | Nilit Plastics | Nylon 66 | FRIANYL® |
| Delene 2070 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |
| NORYL™ SE1GFN1 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |