LUVOCOM® 1500-0871 Datasheet,PSU,LEHVOSS Group-SHANGHAI SUSHENG

Message
LUVOCOM®1500-0871 is a polysulfone (PSU) material containing glass beads. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 1500-0871 are: Flame Retardant Good dimensional stability chemical resistance Heat resistance Hydrolytic stability LUVOCOM®Typical application areas of 1500-0871 are: engineering/industrial accessories

General Information
Filler / Reinforcement	Glass beads
Features	Good dimensional stability Good chemical resistance Heat resistance, high Hydrolysis stability Flame retardancy
Uses	Cam
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.46	g/cm³	ISO 1183
Molding Shrinkage	0.50 - 1.0	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.10	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3800	MPa	ISO 527-2
Tensile Stress (Break)	75.0	MPa	ISO 527-2
Tensile Strain (Yield)	3.5	%	ISO 527-2
Flexural Modulus	3200	MPa	ISO 178
Flexural Stress	105	MPa	ISO 178
Flexural Strain at Flexural Strength	4.7	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	170	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	40	kJ/m²	ISO 179/1fU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	150	°C	UL 746B

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+12	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature - Desiccant Dryer	140	°C
Drying Time - Desiccant Dryer	3.0 - 4.0	hr
Rear Temperature	340 - 360	°C
Middle Temperature	345 - 365	°C
Front Temperature	350 - 370	°C
Nozzle Temperature	350 - 370	°C
Processing (Melt) Temp	355	°C
Mold Temperature	140 - 170	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.05%, otherwise porosity and surface defects (e.g. smearing) may occur. To avoid internal stresses, a low shear load should be used for processing. The parts may be tempered at a later stage to reduce internal stresses. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.05%, otherwise porosity and surface defects (e.g. smearing) may occur. To avoid internal stresses, a low shear load should be used for processing. The parts may be tempered at a later stage to reduce internal stresses. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Category:	PSU , Polysulfone
Manufacturer:	LEHVOSS Group
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	mGDP0Z_LUVOCOM15000871.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Qenos PE HD0490	Qenos Pty Ltd	HDPE	Qenos PE
RTP 104 HB	RTP Company	PP, Unspecified	RTP
Sinpolene MBB3132	Teknor Apex Asia Pacific PTE. LTD.	LDPE	Sinpolene
ESTAPROP H 05100GFC	Cossa Polimeri S.r.l.	PP Homopolymer	ESTAPROP
Sylvin 8280-60 Grey 9583	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin