Pearlthane® D91F65D
| Category: | TPU, Unspecified , Thermoplastic Polyurethane Elastomer |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mGCGQc_Pearlthane-D91F65D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PEARLTHANE® D91F65D is an aliphatic TPU supplied in colourless natural pellets. In addition to typical TPU properties like outstanding abrasion loss, PEARLTHANE® D91F65D offers excellent colour stability upon weather exposure. This product provides high quality film and good transparency. It is especially designed for high performance extrusion and film processes. PEARLTHANE® D91F65D is especially recommended for extrusion applications for exterior automotive parts and a variety of high performance technical parts where weather resistance and transparency are required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.11 | g/cm³ | ASTM D792 |
| 20°C | 1.11 | g/cm³ | ISO 2781 |
| Moisture Content | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 40.0 | mm³ | ISO 4649 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 65 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 527 | ||
| 100% strain | 16.0 | MPa | ASTM D412, ISO 527 |
| 300% strain | 25.0 | MPa | ASTM D412, ISO 527 |
| Tensile Strength (Yield) | 30.0 | MPa | ASTM D412, ISO 527 |
| Tensile Elongation (Break) | 370 | % | ASTM D412, ISO 527 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 140 - 150 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 50.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 155 | °C | |
| Middle Temperature | 160 | °C | |
| Front Temperature | 160 | °C | |
| Nozzle Temperature | 170 | °C | |
| Mold Temperature | 35.0 | °C | |
| Screw L/D Ratio | 23.0:1.0 |
| Injection instructions |
|---|
| Closing force: 30 tonsScrew diameter: 30 mmMaximum hydraulic pressure: 210 barMold Plaque: 120x120x2 mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 50.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 170 - 180 | °C | |
| Cylinder Zone 2 Temp. | 180 - 190 | °C | |
| Cylinder Zone 3 Temp. | 190 - 200 | °C | |
| Cylinder Zone 4 Temp. | 185 - 195 | °C | |
| Die Temperature | 165 - 175 | °C |
| Extrusion instructions |
|---|
| L/D Ratio: 25:1 to 30:1Compression Ratio: 2:1 to 3:1Screw Speed: 12 to 60 rpm |
| Note Message | |
|---|---|
| 1 . | Temperature at which MFI = 10 g/10 min @ 21.6 kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinnolit® P 3468 | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| Axiall PVC 11860 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Ferro PP TPP20AF66WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| OnFlex™ S KE 70A-3E1726 SO10 | PolyOne Corporation | TPE | OnFlex™ |
| Rotuba CAP CP801 (18% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |