LNP™ LUBRICOMP™ RP004 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mG0XXB_LNP-LUBRICOMP-RP004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* RP004 is a compound based on Nylon 66 resin containing 20% PTFE/Silicone. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RL-4540 Product reorder name: RP004 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.84 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.1 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2620 | MPa | ASTM D638 |
| -- | 2730 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 61.0 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2/5 |
| Break 3 | 61.0 | MPa | ASTM D638 |
| Break | 63.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 22 | % | ASTM D638 |
| Yield | 26 | % | ISO 527-2/5 |
| Break 5 | 23 | % | ASTM D638 |
| Break | 27 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2260 | MPa | ASTM D790 |
| -- 7 | 2400 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.020 | ||
| vs. Itself - Static | 0.045 | ||
| Wear Factor - Washer | 3.50 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 8 | 5.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 350 | J/m | ASTM D4812 |
| 23°C 9 | 88 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 6.70 | J | ASTM D3763 |
| -- | 1.20 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 237 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 200 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 64.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 63.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 8.4E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 9.4E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTS PCA-1010HF | Polymer Technology and Services, LLC | PC+ABS | PTS |
| NEFTEKHIM ABS 0475E | Nizhnekamskneftekhim Inc. | ABS | NEFTEKHIM ABS |
| EnviroPro 2014TF13 | West Michigan Compounding | PP, Unspecified | EnviroPro |
| Sylvin 9940-80 NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ALTECH® ABS FC 1000/106 BK1280-05 | ALBIS PLASTIC GmbH | ABS | ALTECH® ABS |