LNP™ STAT-KON™ WEF42I compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mFr3aX_LNP-STAT-KON-WEF42I-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON WEF42I is a compound based on PBT resin containing 10% Carbon Fiber, 20% Glass Fiber. Added features of this grade include: High Impact, Electrically Conductive. Also known as: LNP* STAT-KON* Compound WCF-1006 HI Product reorder name: WEF42I |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.50 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 21800 | MPa | ASTM D638 |
| -- | 15800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 94.0 | MPa | ASTM D638 |
| Break | 99.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.7 | % | ASTM D638 |
| Break | 2.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 9990 | MPa | ASTM D790 |
| -- 5 | 10500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 170 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 126 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 7 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 710 | J/m | ASTM D4812 |
| 23°C 8 | 46 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 16.6 | J | ASTM D3763 |
| -- | 4.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 219 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 203 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 205 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 220 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.1E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.3E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0 to 5.0 | ohms | ASTM D257 |
| Volume Resistivity | 4.0 to 6.0 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201D UV | RTP Company | Nylon 612 | RTP |
| Vyncolit® RX®1-520 | Vyncolit N.V. | DAP | Vyncolit® |
| Generic PPE+PS+Nylon | Generic | PPE+PS+Nylon | Generic |
| HiFill® PA6/6 GF13 IM HS L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| POLYCOMPO PP J108M | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |