NANCAR® 1203LD
| Category: | NBR , Acrylonitrile Butadiene Rubber |
| Manufacturer: | Nantex Industry Co., Ltd. |
| Trademark: | NANCAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mF8PIq_NANCAR-1203LD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NANCAR® 1203LD is a fluxed blend of 70 parts NANCAR NBR and 30 parts polyvinyl chloride. This polymer has sufficient stabilizer for normal aging conditions. Its good processability for extrusion provides smooth surface on the resultant products. NANCAR® 1203LD has excellent resistance to abrasion, ozone, oils and fuels. It is suggested for use in cable jackets, belts, hose covers, shoe soles, shoes and rolls. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mooney Viscosity (ML 1+4, 100°C) | 66 | MU | ASTM D1646 |
| Acrylonitrile Content - Bound | 28.0 | % | Internal Method |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Compression Set - 70 hrs (100°C) | 45 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Loss | 0.30 | % | ASTM D5688 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Ozone Resistance - 50 pphm X 40°C X 20% 1 | no crack |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 72 |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength (Yield) | 12.7 | MPa | |
| Tensile Elongation (Break) | 370 | % |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Change in Tensile Strength in Air (100°C, 70 hr) | 3.0 | % | |
| Change in Ultimate Elongation in Air (100°C, 70 hr) | -38 | % | |
| Change in Durometer Hardness in Air (100°C, 70 hr) | 2.0 | ||
| Change in Tensile Strength | |||
| 100°C, 70 hr, in ASTM #1 Oil | 14 | % | |
| 100°C, 70 hr, in IRM 903 Oil | 12 | % | |
| Change in Ultimate Elongation | |||
| 100°C, 70 hr, in ASTM #1 Oil | -43 | % | |
| 100°C, 70 hr, in IRM 903 Oil | -32 | % | |
| Change in Durometer Hardness | |||
| Shore A, 100°C, 70 hr, in ASTM #1 Oil | 10 | ||
| Shore A, 100°C, 70 hr, in IRM 903 Oil | 2.0 | ||
| Change in Volume | |||
| 100°C, 70 hr, in ASTM Oil #1 | -12 | % | |
| 100°C, 70 hr, in IRM 903 Oil | 2.0 | % |
| Note Message | |
|---|---|
| 1 . | at 24 hrs, 48 hrs, 72 hrs, 96 hrs, 168 hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Axiall PVC 11600 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Elastron® G G601.A50.N | Elastron USA, Inc. | SEBS | Elastron® G |
| HiFill FR® PA6 GF15 FR-N | Techmer Engineered Solutions | Nylon 6 | HiFill FR® |
| Karina IVORY PVC COMPOUND -E 680D35/ 1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polifil® Nylon 628-33GF | The Plastics Group | Nylon 66 | Polifil® Nylon |