Starex GR-5020 T
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mEuY9Z_Starex-GR-5020-T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex GR-5020 T is a Styrene Acrylonitrile (SAN) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 14 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 to 0.30 | % | ASTM D955 |
| Ash Content | |||
| -- | 20 | % | ISO 3451 |
| -- | 20 | % | ASTM D5630 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6300 | MPa | ASTM D638 |
| -- | 6900 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 110 | MPa | ASTM D638 |
| Yield | 119 | MPa | ISO 527-2/50 |
| Break 3 | 110 | MPa | ASTM D638 |
| Break | 119 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 2.5 | % | ASTM D638 |
| Break | 2.4 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 6900 | MPa | ASTM D790 |
| -- 6 | 7700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 110 | MPa | ASTM D790 |
| -- 8 | 158 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 12 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 51 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 50 | J/m | ASTM D256 |
| 23°C 10 | 6.9 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 104 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 105 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 102 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 101 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 106 | °C | ISO 306/B50 |
| -- | 110 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 180 to 190 | °C | |
| Middle Temperature | 200 to 210 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Pressure | 93.2 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zelux® SD-P | Westlake Plastics Company | PC | Zelux® |
| BJB Polyurethane TC-886 A/B FR | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| INNOPOL® PP CS 1-3130 MA | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |
| LNP™ LUBRICOMP™ DFP36 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| TOTAL Polyethylene Lumicene® M 3421 UV | TOTAL Refining & Chemicals | mMDPE | TOTAL Polyethylene |