Techsil 1382 CLEAR
| Category: | Silicone , Silicone |
| Manufacturer: | Techsil Limited |
| Trademark: | Techsil |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mEmIbM_Techsil-1382-CLEAR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Techsil 1382 is a fast cure 1-part RTV silicone sealant specially formulated for applications requiring a combination of good adhesion, excellent physical and non-corrosive properties. The Oxime based cure system produces excellent physical properties and good adhesion particularly to plastics and many other substrates. Although not totally neutral the cured sealant is very low corrosive in nature. Key Features:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | BS 903 |
| Molding Shrinkage - Flow | < 0.80 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 33 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(100% Strain) | 0.800 | MPa | BS 903 |
| Tensile Strength 2(Yield) | 2.15 | MPa | BS 903 |
| Tensile Elongation 3(Break) | 300 | % | BS 903 |
| Tear Strength 4 | 4.80 | kN/m | BS 903 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE | |||
| Flow | 3.0E-4 | cm/cm/°C | |
| Transverse | 8.9E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.20 | W/m/K | |
| Service Temperature 5 | -50 to 220 | °C |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Tack Free Time 6(23°C) | 5.0 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Cure Time 7(23°C, 3.00 mm) | 12.0 | hr | |
| Extrusion Rate | 390 | g/min | |
| Young's Modulus 8 | 0.600 | MPa |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 8.7E+15 | ohms·cm | ASTM D257 |
| Dielectric Constant (1 MHz) | 3.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 2.5E-3 | ASTM D150 |
| Note Message | |
|---|---|
| 1 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| 2 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| 3 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| 4 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| 5 . | AFS 1540B |
| 6 . | 65%RH |
| 7 . | 65%RH |
| 8 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DURANEX® 6300T | Polyplastics Co., Ltd. | PBT | DURANEX® |
| Hyundai EP Breathable AT880H/2102 | HYUNDAI EP Co., Ltd. | Polyolefin, Unspecified | Hyundai EP Breathable |
| Osterlene® PPC10-2.1 | Osterman & Company | PP Impact Copolymer | Osterlene® |
| Sylvin 8600-75 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ THERMOCOMP™ DF004 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |