MARCOBLEND 6000 A BK
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | POLY GIN |
| Trademark: | MARCOBLEND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mEbPIG_MARCOBLEND-6000-A-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MARCOBLEND 6000 A BK is an ignition resistant polycarbonate/ABS resin.The resin is Halogen free and compliance with TCO and RoHS certification. The unique characters include superior processability, High gloss & anti-scratch grade good stiffness, and excellent dimension stability and suitable for use in TFT LCD frame and internal structure parts. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (240°C/5.0 kg) | 40 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 48.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 2450 | MPa | ASTM D790 |
| Flexural Strength | 85.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 110 | °C | |
| 1.8 MPa, Unannealed | 80.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 230 to 240 | °C | |
| Nozzle Temperature | 245 to 255 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® PX10 X06 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| Xuchuan 1003/B-5301 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyether | Xuchuan |
| Evoprene™ 047 | AlphaGary | SBS | Evoprene™ |
| Karina WHITE PVC COMPOUND -E 803-10/ 1-A-RT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Deprene 101-55 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |