Order Products : sales@su-jiao.com
MAGNUM™ 375 HP
| Category: | ABS , ABS Resin |
| Manufacturer: | Trinseo |
| Trademark: | MAGNUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mERD2m_MAGNUM-375-HP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High Heat, Low Gloss, Medium Impact ABS resin for injection molded automotive interior trim applications. Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792, ISO 1183/B |
| Apparent Density | 0.68 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 2.1 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.56 | % | ISO 294-4 |
| Flow direction | 0.57 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2300 | MPa | ASTM D638 |
| -- | 2330 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield 2 | 49.0 | MPa | ASTM D638 |
| Yield | 47.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 3 | 3.1 | % | ASTM D638 |
| Yield | 2.9 | % | ISO 527-2/50 |
| Fracture 4 | 8.8 | % | ASTM D638 |
| Fracture | 3.5 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2410 | MPa | ASTM D790 |
| -- | 2390 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 6 | 76.5 | MPa | ASTM D790 |
| -- | 72.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 11 | kJ/m² | ISO 179/1eA |
| 23°C | 22 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 130 | J/m | ASTM D256 |
| 23°C | 220 | J/m | ASTM D256 |
| -30°C | 10 | kJ/m² | ISO 180/A |
| 23°C | 25 | kJ/m² | ISO 180/A |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Peak Energy | 23.0 | J | ASTM D3763 |
| 23°C, Peak Energy | 30.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 99.4 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 98.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 81.7 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 83.9 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 103 | °C | ISO 306/B50, ASTM D1525 7 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 100°C | 7.7E-5 | cm/cm/°C | ASTM E831 |
| Horizontal : -40 to 100°C | 9.5E-5 | cm/cm/°C | ASTM E831 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| FMVSS Flammability 8 | 30 | mm/min | FMVSS 302 |
| Additional Information |
|---|
| Tests conducted on 0.125 inch (3.2 mm) injection molded specimen, unannealed, unless noted. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.0 - 85.0 | °C | |
| Drying Time | > 2.0 | hr | |
| Rear Temperature | 238 | °C | |
| Middle Temperature | 249 | °C | |
| Front Temperature | 254 | °C | |
| Nozzle Temperature | 249 - 254 | °C | |
| Processing (Melt) Temp | 243 - 271 | °C |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| 5 . | Method I (three-point load), 1.3 mm/min |
| 6 . | Method I (three-point load), 1.3 mm/min |
| 7 . | 速率 A (50°C/h), 载荷2 (50N) |
| 8 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Royalite R60 | Spartech Plastics | PMMA+PVC | Royalite |
| TOPAS® 6013M-07 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
| Xuchuan XCY-5975B | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Gallonprene® GP540-7505C | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Kumho SBR 1500S | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |