XIRAN® SE700 are SMA (styrene maleic anhydride) based compounds especially designed for extrusion processes with:
Application areas XIRAN® SE700 is designed for extrusion processes and designed to optimize the Vicat properties of (high impact) polystyrene. These products are very suitable for painted and foamed parts, high temperature resistance and precision parts with high shot to shot consistency. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/10.0 kg) | 22 | g/10 min | ISO 1133 |
| Spiral Flow 1 | 36.0 | cm | Internal method |
| Molding Shrinkage 2 | Internal method | ||
| Vertical flow direction | 0.50 | % | Internal method |
| Flow direction | 0.20 | % | Internal method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 36.0 | MPa | ISO 527-2 |
| Fracture | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 8500 | MPa | ISO 178 |
| Flexural Stress | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -40°C | 30 | kJ/m² | ISO 179/1eU |
| 23°C | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/A | ||
| -40°C | 5.0 | kJ/m² | ISO 180/A |
| 23°C | 9.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 92.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 115 | °C | ISO 306/B |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -30 to 80°C | 2.9E-5 | cm/cm/°C | ASTM D696 |
| Horizontal : -30 to 80°C | 4.7E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Cylinder Zone 1 Temp. | 230 - 250 | °C | |
| Cylinder Zone 2 Temp. | 230 - 250 | °C | |
| Cylinder Zone 3 Temp. | 230 - 250 | °C | |
| Cylinder Zone 4 Temp. | 230 - 250 | °C | |
| Cylinder Zone 5 Temp. | 230 - 250 | °C |
| Extrusion instructions |
|---|
| Maximum processing temperature: 285°C |
| Note Message | |
|---|---|
| 1 . | 2 mm |
| 2 . | Measured according to the Autodesk Mold flow Plastics Labs using a tag mold. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polymer-E V28280 | Asia Polymer Corporation (APC) | EVA | Polymer-E |
| Sylvin 8303-60 Black | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| XENOY™ 5220U resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |
| Sylvin 8260-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Luranyl® KR 2403 G2 TW 26343 | ROMIRA GmbH | PPE+PS | Luranyl® |