TECHNYL® 1011R BRIGHT
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mChNYI_TECHNYL-1011R-BRIGHT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, Unfilled, lubricated, for injection molding |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.2 to 1.5 | -- | % | |
| Flow | 1.1 to 1.5 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.3 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength (Yield) | 80.0 | -- | MPa | ASTM D638 |
| Tensile Elongation (Break) | 45 | -- | % | ASTM D638 |
| Flexural Modulus | 2950 | -- | MPa | ASTM D790 |
| Flexural Strength (Break) | 115 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 85 | -- | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 60.0 | -- | °C | |
| 1.8 MPa, Unannealed | 180 | -- | °C | |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | 3.4 | 3.9 | kV/mm | IEC 60243-1 |
| Dissipation Factor | 0.020 | 0.10 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 245 | °C | |
| Front Temperature | 245 to 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME HIPS SH825 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
| Yuyao PPO N100A | Yuyao Tenglong Plastics Co., Ltd. | PPE+PS | Yuyao PPO |
| Andur 9000-AP/Curene® 280 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Pebax® MH 2030 | Arkema | PEBA-Ether | Pebax® |
| CYCOLAC™ MG38N resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |