Cevian®-V VF191
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Cevian®-V |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mCMLTY_Cevian--V-VF191.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Cevian®-V VF191 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific. Primary attribute of Cevian®-V VF191: Flame Rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 19 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 113 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 50.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2600 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 6.40 mm | 60 | J/m | |
| 23°C, 6.40 mm | 100 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 12.7 mm | 90.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 79.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 97.0 | °C | ISO 306/B50 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Ball Pressure Test | 90 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.50 mm) | 27 | kV/mm | ASTM D149 |
| Arc Resistance (3.00 mm) | 53.0 | sec | ASTM D495 |
| Arc Resistance (3.00 mm) | PLC 7 | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.70 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 180 to 190 | °C | |
| Middle Temperature | 200 to 210 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 220 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 5.00 to 15.0 | MPa | |
| Screw Speed | 40 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene CPP2030 | Teknor Apex Asia Pacific PTE. LTD. | PP Copolymer | Sinpolene |
| Titalon® 3225AF | Titan Plastics Compounds Co., Ltd. | Nylon 12 | Titalon® |
| Colorite CS Series CS7559LS | Colorite Polymers | PVC, Flexible | Colorite CS Series |
| LNP™ LUBRICOMP™ EFL36XXC compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |
| REV Materials 8001-002 | REV Materials | PP, Unspecified | REV Materials |