Lucene™ LC170
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mCCx5O_Lucene-LC170.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LUCENE LC170 is an ethylene-octene copolymer produced using LG Chem's metallocene polymerization catalyst and solution process technology. This resin is an excellent impact modifier for plastics and offers unique performance capabilities for compounded products. Applications
Performance
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.870 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.1 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 23 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 71 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 9.50 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | > 900 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 14.0 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 3 | 40.0 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -53.0 | °C | Internal Method |
| Melting Temperature (DSC) | 58.0 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| apilon 52® TL 50 | API SpA | TPU-Polyether | apilon 52® |
| DAPCO™ 3003 | Cytec Industries Inc. | Epoxy | DAPCO™ |
| Exelene® HDPE 6007 | Montachem International, Inc. | HDPE | Exelene® HDPE |
| Hyundai EP PA66 LD240 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| LNP™ LUBRICOMP™ KI001XXJ compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |