AVP™ RLL20CP
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | AVP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mC1u2y_AVP-RLL20CP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AVP™ RLL20CP is a Polycarbonate (PC) product filled with 20% glass fiber. It can be processed by injection molding and is available in North America. Applications of AVP™ RLL20CP include electrical/electronic applications, appliances and automotive. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.18 mm) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5790 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 110 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 5380 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 91 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 143 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Drying Time, Maximum | 16 | hr | |
| Rear Temperature | 282 to 304 | °C | |
| Middle Temperature | 293 to 316 | °C | |
| Front Temperature | 304 to 338 | °C | |
| Nozzle Temperature | 304 to 327 | °C | |
| Processing (Melt) Temp | 310 to 338 | °C | |
| Mold Temperature | 82.2 to 116 | °C | |
| Back Pressure | 0.345 to 1.38 | MPa | |
| Screw Speed | 50 to 75 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLPLAST TC 2000B | UTEKSOL d.o.o. | SBS | SOLPLAST TC |
| COPYLENE® CR300CL-01 | Phillips 66 | PP Random Copolymer | COPYLENE® |
| KYOCERA KE-G200V | KYOCERA Chemical Corporation | Epoxy | KYOCERA |
| LNP™ LUBRICOMP™ RL0039XP compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| OPNYL OP66UT105 | Ovation Polymers Inc. | Nylon 66 | OPNYL |