RTV-2 GI-384
| Category: | Silicone Rubber, RTV-2 , Silicone Rubber, RTV-2 |
| Manufacturer: | Silicones, Inc. |
| Trademark: | RTV-2 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mBtW0O_RTV-2-GI-384.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GI-384 is a high tear strength, tin-catalyzed RTV-2 silicone rubber, which was designed for casting solid polyurethane resins, polyurethane foams and other plastic parts. GI-384 is not sensitive to inhibition, meaning it will cure at room temperature over virtually any surface. It is easy to mix and de-air, and will cure with only a slight degree of shrinkage. The speed at which the rubber hardens can be accelerated with special activators. GI-384 is extremely useful for those applications where a strong flexible rubber is required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | |
| Shrinkage - Cured | 0.10 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature - Cured | -51 to 177 | °C |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coverage - Cured | 0.910 | cm³/g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 5.0 Mix Ratio by Volume: 5.6 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity 1 | 10000 to 20000 | cP |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 2 | Red | ||
| -- 3 | White | ||
| Viscosity | |||
| -- 4 | 0.30 to 0.40 | Pa·s | |
| -- 5 | 25 to 40 | Pa·s | |
| Curing Time | 16 to 18 | hr | |
| Pot Life | 60 to 120 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | |||
| Shore A 6 | 21 to 29 | ||
| Shore A 7 | 26 to 34 | ||
| Tensile Strength | 2.93 to 3.28 | MPa | ASTM D412 |
| Tensile Elongation at Break | 400 to 450 | % | ASTM D412 |
| Tear Strength | 17.5 to 26.3 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Mixed |
| 2 . | Activator |
| 3 . | Base |
| 4 . | Activator |
| 5 . | Base |
| 6 . | 1 Day |
| 7 . | 7 Days |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACLAR® 11A (4 mil) | Honeywell | PCTFE | ACLAR® |
| BP RPP 1310 T NAT | Buckeye Polymers, Inc. | PP, Unspecified | BP |
| BULKSAM® TM-25M | UMG ABS, Ltd. | ABS | BULKSAM® |
| GPPC ABS D-120F | GPPC Chemical Co., Ltd. | ABS | GPPC ABS |
| Sylvin 8398-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |