Innothane® IE-60DC
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | Innothane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m8zkym_Innothane-IE-60DC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-60DC is a tough, abrasion resistant elastomer formulated for room temperature hand-batch processing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.06 | g/cm³ | |
| Cured | 1.10 | g/cm³ | |
| Base Resin | 1.12 | g/cm³ | |
| Molding Shrinkage - Flow | 0.020 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 103 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 60.0 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 13 Mix Ratio by Weight: 12 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 120 to 240 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Exotherm - 200g mass | 49 | °C |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.25 | Pa·s | |
| 25°C 2 | 2.2 | Pa·s | |
| 25°C 3 | 2.8 | Pa·s | |
| Curing Time (25°C) | 24 | hr | |
| Gel Time | 9.0 to 13 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 35 to 45 | ASTM D2240 | |
| Tensile Strength | 11.9 | MPa | ASTM D638 |
| Tensile Elongation at Break | 190 | % | ASTM D638 |
| Tear Strength | 36.8 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC GA-3099 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| Stat-Tech™ ST9620-0020 ES Red | PolyOne Corporation | LCP+PPS | Stat-Tech™ |
| Ultramid® A3EG3 | BASF Corporation | Nylon 66 | Ultramid® |
| Arnitel® EL250 | DSM Engineering Plastics | TPC-ET | Arnitel® |
| Sylvin 83028-90 Yellow 4202 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |