LEXAN™ SLD3000 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m8Fys8_LEXAN-SLD3000-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Antistatic colorable/opaque FR PC grade |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 19 | g/10 min | ASTM D1238 |
| Molding Shrinkage 1 | Internal Method | ||
| Flow | 0.40 | % | |
| Across Flow | 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 52.0 | MPa | ASTM D638 |
| Tensile Strain (Break) | 200 | % | ISO 527-2/50 |
| Flexural Modulus | 2040 | MPa | ASTM D790 |
| Flexural Strength (Yield, 6.40 mm) | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 700 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 100 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.2E+12 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.500 mm | HB | ||
| 1.00 mm | V-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 30 to 80 | % | |
| Rear Temperature | 220 to 245 | °C | |
| Middle Temperature | 220 to 255 | °C | |
| Front Temperature | 230 to 260 | °C | |
| Nozzle Temperature | 230 to 260 | °C | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 30.0 to 70.0 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.38 to 0.76 | mm |
| Note Message | |
|---|---|
| 1 . | 1.5 to 3.2 mm |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP800-706UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Fluon® PTFE G190 | Asahi Glass Co., Ltd. | PTFE | Fluon® |
| ENGAGE™ 8407 | The Dow Chemical Company | TPO (POE) | ENGAGE™ |
| HIVOREX 5200SU | Lotte Chemical Corporation | HDPE | HIVOREX |
| Sylvin 916VO-85 Grey 9542 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |