Ferro PP TPP30AE84HB WHITE
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m7EhwK_Ferro-PP-TPP30AE84HB-WHITE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ferro PP TPP30AE84HB WHITE is a Polypropylene Homopolymer (PP Homopolymer) material filled with 30% talc. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Primary attribute of Ferro PP TPP30AE84HB WHITE: Homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.4 | % | |
| Across Flow | 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 33.1 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 10 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : 23°C | 2450 | MPa | |
| Tangent : 23°C | 3010 | MPa | |
| Flexural Strength (23°C) | 51.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 27 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 510 | J/m | ASTM D4812 |
| Gardner Impact (23°C) | 0.565 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 128 | °C | |
| 1.8 MPa, Unannealed | 73.9 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POWERSIL® 3525 VP | Wacker Chemie AG | Silicone | POWERSIL® |
| REPOL® R110MK | Reliance Industries Limited | PP Random Copolymer | REPOL® |
| DINALON® PA 6.6 40% FV | Grupo Repol | Nylon 66 | DINALON® |
| DIC.PPS FZ-6600-A5 | DIC Corporation | PPS | DIC.PPS |
| LIHAN® T9703EP | Nanjing Lihan Chemical Co., Ltd. | PBT | LIHAN® |