Aplax P1013GN
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ginar Technology Co., LTD. |
| Trademark: | Aplax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m7C7KF_Aplax-P1013GN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aplax P1013GN is a 50 % talcum reinforced PP product for injection moulding in natural colour |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (1.60 mm) | 0.60 - 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 36.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 7240 | MPa | ISO 178 |
| Flexural Stress | 69.0 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 145 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | > 165 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Additional Information |
|---|
| Notched Izod Impact Strength, ISO 180/1, notch 0.25in: 32 kg cm/cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 170 - 220 | °C | |
| Middle Temperature | 170 - 220 | °C | |
| Front Temperature | 170 - 220 | °C | |
| Processing (Melt) Temp | 180 - 220 | °C | |
| Injection Pressure | 50.0 - 120 | MPa | |
| Holding Pressure | 30.0 - 80.0 | MPa | |
| Back Pressure | 0.00 - 0.300 | MPa | |
| Screw Speed | 60 - 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® F7895 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Generic PS (HIPS) | Generic | PS (HIPS) | Generic |
| Gravi-Tech™ GRV-UR-045-SS-W Black | PolyOne Corporation | PUR, Unspecified | Gravi-Tech™ |
| LG ABS AP163 | LG Chem Ltd. | ABS | LG ABS |
| Karina IVORY PVC COMPOUND -E 856-35/ 1-DY-IS(AF-70)/K | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |