LNP™ THERMOCOMP™ OF008A compound
| Category: | PPS , Branched Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m7Be5o_LNPTHERMOCOMPOF008Acompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP OF008A is a compound based on PPS - Branched resin containing Glass Fiber.This product is also known as THERMOCOMP* OF-1008. Also known as: LNP* THERMOCOMP* Compound OF-1008 Product reorder name: OF008A |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.20 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture 1 | 178 | MPa | ASTM D638 |
| Fracture | 160 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 2 | 1.7 | % | ASTM D638 |
| Fracture | 1.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 3 | 14300 | MPa | ASTM D790 |
| -- 4 | 13400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 190 | MPa | ISO 178 |
| Yield, 50.0mm span 5 | 248 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 100 | J/m | ASTM D256 |
| 23°C 6 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 590 | J/m | ASTM D4812 |
| 23°C 7 | 21 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 261 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 8 | 272 | °C | ISO 75-2/Af |
| CLTE - Flow (23 to 60°C) | 2.6E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 - 316 | °C | |
| Middle Temperature | 321 - 332 | °C | |
| Front Temperature | 332 - 343 | °C | |
| Processing (Melt) Temp | 316 - 321 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4641P | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Ultralloy™ 203 | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| Ultramid® T KR 4355 G10 | BASF Corporation | Nylon 6/6T | Ultramid® |
| NuSil R-2370 | NuSil Technology | Silicone | NuSil |
| Karina CLEAR PVC COMPOUND -E 70/239-AT-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |