Kingfa HG-105
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m6564m_Kingfa-HG-105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa HG-105 is a polypropylene material, which contains a 25% filler. This product is available in North America or Asia Pacific,. The main features of Kingfa HG-105 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 1.3 - 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 101 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, Injection Molded) | 31.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, Injection Molded) | 80 | % | ASTM D638 |
| Flexural Modulus 3(23°C, Injection Molded) | 1710 | MPa | ASTM D790 |
| Flexural Strength 4(23°C, Injection Molded) | 35.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 54 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm, injection molding | 137 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm, injection molding | 74.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Additional Information |
|---|
| Filler Content, ISO3451/1, Method A: 25% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AA36NT6503 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Hyundai EP TOP COAT PT900W / 2101 | HYUNDAI EP Co., Ltd. | PP, Unspecified | Hyundai EP TOP COAT |
| LTP ZW-3600 | Chengdu Letian Plastics Co., Ltd | PPS Alloy | LTP |
| OmniCarb™ PC08FR510 | OMNI Plastics, LLC | PC | OmniCarb™ |
| Softell TKG 300N 1 D62819 | LyondellBasell Industries | PP Copolymer | Softell |