VICTREX® PEEK 600G

Category:	PEEK , Polyetheretherketone
Manufacturer:	Victrex plc
Trademark:	VICTREX® PEEK
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	m63oWK_VICTREX-PEEK-600G.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, low flow, FDA food contact compliant, colour natural/beige.

Applications for higher strength and stiffness as well as high ductility. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.

General Information
Features	Semicrystallization Rigidity, high High strength Good disinfection Low liquidity Good chemical resistance Compliance of Food Exposure ductility
Uses	Non-specific food applications Medical/nursing supplies
Agency Ratings	FDA Food Exposure, Not Rated
Appearance	Beige Natural color
Forms	Particles
Processing Method	Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Density			ISO 1183
-- ¹	1.26	g/cm³	ISO 1183
-- ²	1.30	g/cm³	ISO 1183
Spiral Flow	8.50	cm	Internal method
Molding Shrinkage ³			ISO 294-4
Vertical flow direction	1.3	%	ISO 294-4
Flow direction	1.0	%	ISO 294-4
Water Absorption			ISO 62
23°C, 24 hr, 3.20 mm	0.070	%	ISO 62
Balance, 23°C, 3.20mm, 50% RH	0.40	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	3700	MPa	ISO 527-2
Tensile Stress (Yield, 23°C)	95.0	MPa	ISO 527-2
Tensile Strain (Break, 23°C)	45	%	ISO 527-2
Flexural Modulus (23°C)	4100	MPa	ISO 178
Flexural Stress			ISO 178
3.5% strain, 23°C	115	MPa	ISO 178
23°C ⁴	155	MPa	ISO 178
125°C	80.0	MPa	ISO 178
175°C	17.0	MPa	ISO 178
275°C	12.0	MPa	ISO 178
Compressive Stress			ISO 604
23°C	120	MPa	ISO 604
120°C	70.0	MPa	ISO 604

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	9.5	kJ/m²	ISO 180/A
Unnotched Izod Impact Strength (23°C)	No Break		ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	152	°C	ISO 75-2/Af
Glass Transition Temperature	143	°C	ISO 11357-2
Melting Temperature	343	°C	ISO 11357-3
Linear thermal expansion coefficient			ISO 11359-2
Flow : < 143°C	3.5E-4	cm/cm/°C	ISO 11359-2
Flow : > 143°C	1.5E-3	cm/cm/°C	ISO 11359-2
Lateral : < 143°C	5.5E-4	cm/cm/°C	ISO 11359-2
Lateral : > 143°C	1.4E-3	cm/cm/°C	ISO 11359-2
Specific Heat (23°C)	2200	J/kg/°C	ASTM C351
Thermal Conductivity (23°C)	0.29	W/m/K	ISO 22007-4

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity			IEC 60093
23°C	1.0E+16	ohms·cm	IEC 60093
125°C	1.0E+15	ohms·cm	IEC 60093
275°C	1.0E+9	ohms·cm	IEC 60093
Dielectric Strength (2.00 mm)	23	kV/mm	IEC 60243-1
Dielectric Constant			IEC 60250
23°C, 50 Hz	3.20		IEC 60250
200°C, 50 Hz	4.50		IEC 60250
Dissipation Factor (23°C, 1 MHz)	3.0E-3		IEC 60250
Comparative Tracking Index	150	V	IEC 60112

Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity (400°C)	450	Pa·s	ISO 11443

Injection	Nominal Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	3.0 - 5.0	hr
Hopper Temperature	< 100	°C
Rear Temperature	370	°C
Middle Temperature	375 - 380	°C
Front Temperature	385	°C
Nozzle Temperature	390	°C
Mold Temperature	190 - 220	°C

Injection instructions
Runner: Die / nozzle >3mm, manifold >3.5mmGate: >1mm or 0.5 x part thickness

Note Message
1 .	Amorphous
2 .	Crystalline
3 .	390°C nozzle, 200°C tool
4 .	at Yield

Resin Grade	Manufacturer	Category	Trademark
AKROMID® B3 GFM 10/20 natural (3692)	AKRO-PLASTIC GmbH	Nylon 6	AKROMID®
Arak PP EP2X83CE	Shazand (Arak) Petrochemical Corporation	PP Random Copolymer	Arak PP
DJSilicone NE-5140	DONGJUE SILICONE (NANJING) CO., LTD	Silicone	DJSilicone
FERREX® GPP20CK HB-BK	Ferro Corporation	PP, Unspecified	FERREX®
KOPET® KP132FR	Kolon Plastics, Inc.	PET	KOPET®