Ryton® BR42B
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Ryton® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m5rgNy_Ryton-BR42B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ryton® BR42B 40% glass fiber reinforced polyphenylene sulfide compound is specially formulated to provide low coefficient of friction and reduced wear rate for use in applications requiring low surface friction and/or wear. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.76 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 3.20 mm | 0.20 | % | |
| Across Flow : 3.20 mm | 0.50 | % | |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 97 | ||
| R-Scale | 117 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 186 | MPa | ASTM D638 |
| -- | 190 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 1.6 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 14500 | MPa | ASTM D790 |
| -- | 14000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 269 | MPa | ASTM D790 |
| -- | 280 | MPa | ISO 178 |
| Compressive Strength | 255 | MPa | ASTM D695 |
| Poisson's Ratio | 0.40 | ||
| Coefficient of Friction 1(vs. Steel - Dynamic) | 0.32 | ASTM D3702 | |
| Wear Rate 2 | 1.60E-6 | m/hr | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 3.18 mm | 91 | J/m | ASTM D256 |
| -- | 9.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact | |||
| 3.18 mm | 750 | J/m | ASTM D4812 |
| -- | 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 265 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -50 to 50°C | 1.5E-5 | cm/cm/°C | |
| Flow : 100 to 200°C | 1.0E-5 | cm/cm/°C | |
| Transverse : -50 to 50°C | 4.0E-5 | cm/cm/°C | |
| Transverse : 100 to 200°C | 8.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.33 | W/m/K | |
| UL Temperature Rating | 180 | °C | UL 746B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 25°C, 1 kHz | 3.70 | ||
| 25°C, 1 MHz | 3.70 | ||
| Dissipation Factor | ASTM D150 | ||
| 25°C, 1 kHz | 2.0E-3 | ||
| 25°C, 1 MHz | 3.0E-3 | ||
| Comparative Tracking Index (CTI) | 150 | V | UL 746 |
| Insulation Resistance 3(90°C) | 1.0E+11 | ohms |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Oxygen Index | 48 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | Against 52100 steel; 100 hrs; 250 psi; 36 rpm; dry; ambient temperature; PV=2500 |
| 2 . | Against 52100 steel; 100 hrs; 250 psi; 36 rpm; dry; ambient temperature; PV=2500 |
| 3 . | 95%RH, 48 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POYAD VM111 | Pooya Polymer Tehran | PP, Unspecified | POYAD |
| SLOVAMID® 66 GF 50 HTS | Plastcom | Nylon 66 | SLOVAMID® 66 |
| YUPLENE® H230P | SK Global Chemical | PP Homopolymer | YUPLENE® |
| Abstron IMG 1120 | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Sylvin 6181-89 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |