LEXAN™ EX1632T resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m55UGt_LEXANEX1632Tresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN EX1632T polycarbonate resin is designed for use in multi-wall sheet or profile extrusion applications. It contains branched polycarbonate resin, release, and UV stabilizer. It is available in a limited number of colors. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2220 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 61.0 | MPa | ASTM D638 |
| Fracture | 57.0 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 6.3 | % | ASTM D638 |
| Fracture | 99 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2370 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 99.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 150 | J/m | ASTM D256 |
| 23°C | 800 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 74.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 140 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 130 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 145 | °C | ASTM D1525 6 |
| -- | 147 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 6.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 6.6E-5 | cm/cm/°C | ASTM E831 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm, Testing by SABIC) | HB | UL 94 |
| Extrusion instructions |
|---|
| Multiwall Sheet Extrusion Parameters: Adapter Temperature: 220 - 260 C Barrel - Zone 1 Temperature: 240 - 270 C Barrel - Zone 2 Temperature: 240 - 270 C Barrel - Zone 3 Temperature: 240 - 270 C Calibrator Temperature: 50 - 100 C Die Temperature: 220 - 280 C Drying Temperature: 120 C Drying Time: 2 - 4 hrs Hopper Temperature: 100 - 120 C Melt Temperature: 220 - 280 C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reon 60-11 | Reliance Industries Limited | PVC Homopolymer | Reon |
| HiFill® MD 90-80039 GY | Techmer Engineered Solutions | HDPE, HMW | HiFill® |
| LACEA® H-100J (Stretched) | Mitsui Chemicals, Inc. | PLA | LACEA® |
| OTECH PVC OW134 - Automotive Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| Sylvin 8230-85LGFUV Grey 9582 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |