Halene H P5200UV
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m5570N_Halene-H-P5200UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
P5200UV is a pipe grade HDPE, produced by the Mitsui CX Technology. P5200UV is stabilized adequately with HALS+ to give a long service life under outdoor exposure and recommended for telecom ducts. P5200UV combines excellent processability with good creep resistance, ESCR and mechanical properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.948 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.80 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (10% Igepal, Compression Molded, F50) | > 1000 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D638 | ||
| Yield, Compression Molded | 25.0 | MPa | |
| Break, Compression Molded | 38.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, Compression Molded | 7.0 | % | |
| Break, Compression Molded | 750 | % | |
| Flexural Modulus (Compression Molded) | 900 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Compression Molded) | 180 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 67.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 121 | °C | ASTM D1525 4 |
| Oxidation Induction Time | > 30 | min | ASTM D3895 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 to 180 | °C | |
| Cylinder Zone 2 Temp. | 150 to 180 | °C | |
| Cylinder Zone 3 Temp. | 150 to 180 | °C | |
| Cylinder Zone 4 Temp. | 150 to 180 | °C | |
| Cylinder Zone 5 Temp. | 150 to 180 | °C | |
| Die Temperature | 170 to 180 | °C |
| Note Message | |
|---|---|
| 1 . | 27°C |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Clear Cote™ TECHNO-COTE™ | Club Kit, Inc. | Epoxy | Clear Cote™ |
| Generic PBT+PET | Generic | PBT+PET | Generic |
| Karina MB CONCENTRADO FC-ZN-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PermaStat® 301 TFE 10 | RTP Company | PC | PermaStat® |
| LNP™ LUBRICOMP™ KFL23LH compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |