Makrolon® 1260
| Category: | PC , Polycarbonate |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makrolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m4ExnF_Makrolon-1260.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MVR (300 °C/1.2 kg) 34 cm³/10 min; impact modified; low viscosity; easy release; injection molding - melt temperature 280 - 320 °C; available in light colors only |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.20 | g/cm³ | ISO 1183 |
| Apparent Density 1 | 0.64 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 36 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 33.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow | 0.50 to 0.70 | % | ISO 2577 |
| Flow | 0.50 to 0.70 | % | ISO 2577 |
| Across Flow : 2.00 mm 2 | 0.70 | % | ISO 294-4 |
| Flow : 2.00 mm 3 | 0.65 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.30 | % | |
| Equilibrium, 23°C, 50% RH | 0.12 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 114 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2350 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 63.0 | MPa | |
| Break, 23°C | 55.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 5.8 | % | |
| Break, 23°C | 100 | % | |
| Nominal Tensile Strain at Break (23°C) | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 4(23°C) | 2350 | MPa | ISO 178 |
| Flexural Stress 5 | ISO 178 | ||
| 3.5% Strain, 23°C | 72.0 | MPa | |
| 23°C | 93.0 | MPa | |
| Flexural Strain at Flexural Strength (23°C) 6 | 6.8 | % | ISO 178 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate - US-FMVSS (> 1.00 mm) | passed | ISO 3795 | |
| Flash Ignition Temperature | 460 | °C | ASTM D1929 |
| Needle Flame Test | IEC 60695-11-5 | ||
| Method F : 1.50 mm | 1.0 | min | |
| Method F : 2.00 mm | 2.0 | min | |
| Method F : 3.00 mm | 2.0 | min | |
| Method K : 1.50 mm | 0.1 | min | |
| Method K : 2.00 mm | 0.1 | min | |
| Method K : 3.00 mm | 0.2 | min | |
| Self Ignition Temperature | 540 | °C | ASTM D1929 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Electrolytical Corrosion (23°C) | A1 | IEC 60426 | |
| ISO Shortname | ISO 7391-PC,MPR,(,,)-24-9 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7 | ISO 7391 | ||
| -30°C, Complete Break | 14 | kJ/m² | |
| 23°C, Partial Break | 55 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -60°C | No Break | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength 8 | ISO 7391 | ||
| -30°C, Complete Break | 15 | kJ/m² | |
| 23°C, Partial Break | 50 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30°C | 55.0 | J | |
| 23°C | 50.0 | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | ||
| -30°C | 5700 | N | |
| 23°C | 4800 | N |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 122 | °C | ISO 75-2/A |
| Glass Transition Temperature 9 | 142 | °C | ISO 11357-2 |
| Vicat Softening Temperature | |||
| -- | 142 | °C | ISO 306/B50 |
| -- | 143 | °C | ISO 306/B120 |
| Ball Pressure Test (134°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 7.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 7.0E-5 | cm/cm/°C | |
| Thermal Conductivity 10(23°C) | 0.20 | W/m/K | ISO 8302 |
| RTI Elec (1.50 mm) | 125 | °C | UL 746 |
| RTI Imp (1.50 mm) | 105 | °C | UL 746 |
| RTI Str (1.50 mm) | 115 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 34 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.10 | ||
| 23°C, 1 MHz | 3.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 1.0E-3 | ||
| 23°C, 1 MHz | 0.010 | ||
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | 250 | V | |
| Solution B | 125 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm | 875 | °C | |
| 1.50 mm | 900 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 875 | °C | |
| 1.50 mm | 875 | °C | |
| 3.00 mm | 900 | °C | |
| Oxygen Index 11 | 30 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Pellets |
| 2 . | 60x60x2 mm, 500 bar |
| 3 . | 60x60x2 mm, 500 bar |
| 4 . | 2.0 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 2 mm/min |
| 7 . | Based on ISO 179-1eA, 3 mm |
| 8 . | Based on ISO 180-A, 3 mm |
| 9 . | 10°C/min |
| 10 . | Cross-flow |
| 11 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ABS VM-1 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| TEREZ PA 6.6 7500 GF 20 GK 10 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| New-prene™ 8265N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| Lionpol HF-210573 | Lion Polymers Incorporated | TPE | Lionpol |
| Magnobond 104-228 | Magnolia Plastics, Inc. | Epoxy | Magnobond |