Tarnamid® T- 27 MCS I8
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Grupa Azoty S.A. |
| Trademark: | Tarnamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m4BwRZ_Tarnamid-T--27-MCS-I8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High viscosity polyamide 6, impact modified. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.11 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 20.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 2.00 mm | 1.5 | -- | % | |
| Flow : 2.00 mm | 2.0 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 9.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.5 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 135 | 60.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2600 | 1000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 72.0 | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 50 | > 200 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2100 | 700 | MPa | ISO 178 |
| Flexural Stress 2 | 76.0 | 20.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -- | 12 | 20 | kJ/m² | |
| -30°C | 8.0 | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -- | No Break | No Break | ||
| -30°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 180 | -- | °C | ISO 306/B |
| Melting Temperature | 221 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+16 | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | 1.0E+13 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (3.20 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Max Regrind | 50 | % | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 80.0 to 110 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP225N | LyondellBasell Industries | PP Random Copolymer | Moplen |
| NANCAR® 2845 | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| DURACON® JW-03 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| Infino TK-6036H | SAMSUNG SDI CO., LTD. | PPA | Infino |
| Sylvin 29168-50 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |