Tisester® PBT UNR FR
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Tisan |
| Trademark: | Tisester® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m41rRy_Tisester-PBT-UNR-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tisester® PBT UNR FR is a Polybutylene Terephthalate (PBT) material. It is available in Africa & Middle East or Europe for injection molding. Important attributes of Tisester® PBT UNR FR are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 1.6 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 80 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 50.0 | MPa | |
| Break | 51.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.9 | % | |
| Break | 5.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 4.5 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 165 | °C | ISO 75-2/Be |
| Vicat Softening Temperature | 175 | °C | ISO 306/B120 |
| Melting Temperature | 225 to 230 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (3.00 mm) | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 220 to 225 | °C | |
| Middle Temperature | 220 to 225 | °C | |
| Front Temperature | 220 to 225 | °C | |
| Nozzle Temperature | 225 | °C | |
| Processing (Melt) Temp | 220 to 230 | °C | |
| Mold Temperature | 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide AG10K | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| FARALLOY® PE-201 | O'Neil Color and Compounding | HDPE | FARALLOY® |
| Karina IVORY PVC COMPOUND 938-35/ 1-BY-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ EX02598C compound | SABIC Innovative Plastics | PEI | LNP™ STAT-KON™ |
| VALOX™ V8280 resin | SABIC Innovative Plastics | PBT+PET | VALOX™ |