TOTAL Polyethylene LDPE 1022 FN 24
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m3iNxB_TOTAL-Polyethylene-LDPE-1022-FN-24.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LDPE 1022 FN 24 is a low density polyethylene made by a high pressure autoclave process. Grade adapted to the production of flexible parts with a high production rate. Application examples: caps, closures, lids, household items, master-batches. LDPE 1022 FN 24 is suited to many applications in the field of consumer, industrial, food or hygiene packaging such as bags, lamination and coextrusion film. |
| General Information | |
|---|---|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.3 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 47 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 260 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 10.0 | MPa | |
| Break | 11.0 | MPa | |
| Tensile Strain (Break) | 520 | % | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Film Thickness - Recommended / Available | 25 to 150 µm | ||
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, Blown Film | 12.0 | MPa | |
| TD : Yield, 40 µm, Blown Film | 11.5 | MPa | |
| MD : Break, 40 µm, Blown Film | 22.0 | MPa | |
| TD : Break, 40 µm, Blown Film | 20.0 | MPa | |
| Dart Drop Impact | 95 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 40.0 µm | 75.0 | kN/m | |
| TD : 40.0 µm | 62.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 94.0 | °C | ISO 306 |
| Melting Temperature | 109 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (40.0 µm, Blown Film) | 7.0 | % | ISO 14782 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 to 250 | °C | |
| Mold Temperature | 30.0 to 40.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 190 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx CPP5B30 | The Matrixx Group, Inc. | PP Copolymer | Matrixx |
| Small Boss SPVC001 | Tongxiang Small Boss Special Plastic Products Co., Ltd. | PVC, Flexible | Small Boss |
| TPUCO® TPUI-L95 | Taiwan PU Corporation | TPU-Polyether | TPUCO® |
| Envirez® MR 80220 | Ashland Performance Materials | Polyester, TS | Envirez® |
| Hostacom BB 174 G | LyondellBasell Industries | PP Copolymer | Hostacom |